Stoneware Clay #50

GoldArt    70
Bell Dark ball clay    20
Redart    10

QIT Red Dust      1

Grog (48 mesh)      5

Na2O  0.2%    Al2O3 30.4%     SiO2 62.5%

K2O  1.3%                              P2O5  0.0%

MgO  0.4%                             TiO2  2.0%

CaO  0.2%                              Fe2O3  3.0%

  

Loss On Ignition:  8.6%

Shrinkage : 13%

Color : Medium brown

Water absorption : 1%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

------------------------------

Stoneware Clay #51

GoldArt    50
Bell Dark ball clay    20
Custer feldspar    10
Silica    10

QIT Red Dust      1.5
Grog (48 mesh)      5

Na2O  0.5%    Al2O3 26.6%     SiO2 66.3%
K2O  1.8%                             TiO2  1.6%
MgO  0.2%                            Fe2O3  2.6%
CaO  0.2%                            

Loss On Ignition:  7.0%

Shrinkage : 13%
Color : Medium brown
Water absorption : 1%
Plasticity : 10.5 (12)
Glaze behaviour : 12 (12)

--------------------------------

Stoneware Clay  #52

GoldArt    60

Bell Dark ball clay    20

Custer feldspar    10

Silica    10

QIT Red Dust      1.8

Grog (48 mesh)      5

Na2O  0.5%    Al2O3 27.0%      SiO2 65.9%
K2O  1.8%                               TiO2  1.7%
MgO  0.2%                              Fe2O3  2.8%
CaO  0.2%                            

Loss On Ignition:  7.2%

Shrinkage : 14%
Color : Medium brown
Water absorption : 2.4%
Plasticity : 10.5 (12)
Glaze behaviour : 12 (12)

------------------------------

Stoneware Clay #53

GoldArt    35
M&D Sledge ball clay    18
Redart    27
Custer feldspar      5
Silica    15

QIT Red Dust      0.25

Grog (48 mesh)      5

Na2O  0.4%    Al2O3 22.8%     SiO2 69.2%

K2O  2.2%                              P2O5  0.1%

MgO  0.6%                             TiO2  1.3%

CaO  0.2%                             Fe2O3  3.3%

                         

Loss On Ignition:  6.1%

Shrinkage : 14%

Color : Dark brown

Water absorption : 1.5%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

-----------------------------

Stoneware Clay #54

GoldArt    38

M&D Sledge ball clay    16

Redart    23

Custer feldspar      5

Silica    18

Grog (48 mesh)      5

Na2O  0.4%    Al2O3 22.5%     SiO2 70.3%

K2O  2.0%                              P2O5  0.1%

MgO  0.6%                             TiO2  1.3%

CaO  0.2%                              Fe2O3  2.7%

Loss On Ignition:  6.0%

Shrinkage : 14%

Color : Dark brown

Water absorption : 1.5%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

-----------------------------

Stoneware Clay #55

GoldArt    53

M&D Sledge ball clay    22

Custer feldspar      5

Silica    20

QIT Red Dust      1.8

Grog (48 mesh)      5

Na2O  0.3%    Al2O3 24.6%     SiO2 68.9%

K2O  1.2%                              TiO2  1.4%

MgO  0.3%                             Fe2O3  3.0%

CaO  0.3%                              

                            

Loss On Ignition:  6.7%

Shrinkage : 14%

Color : Light brown

Water absorption : 1.5%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

-----------------------------

Stoneware Clay #56

EPK    40
M&D Sledge ball clay    30
Silica    15
Custer feldspar      2.5
Talc    12.5

QIT Red Dust      2
Grog (48 mesh)      5

Na2O  0.2%    Al2O3 26.9%     SiO2 62.9%
K2O  0.6%                              P2O5  0.1%
MgO  4.1%                             TiO2  0.7%
CaO  1.4%                              Fe2O3  3.0%
                           

Loss On Ignition:  8.8%

Shrinkage : 14%
Color : Buff
Water absorption : 7%
Plasticity : 10.5 (12)
Glaze behaviour : 12 (12)

-----------------------------

Stoneware Clay #57

GoldArt    50

Bell Dark ball clay    20

Custer feldspar    18.5

Silica    11.5

QIT  RedDust      1.8

Grog (48 mesh)      5

Na2O  0.7%    Al2O3 25.4%       SiO2 66.9%

K2O  2.5%                               TiO2  1.5%

MgO  0.2%                              Fe2O3  2.6%

CaO  0.2%                              

Loss On Ignition:  6.3%

Shrinkage : 14%

Color : Medium brown

Water absorption : 0.1%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

------------------------------

Stoneware Clay #58

GoldArt    50

Bell Dark ball clay    20

Custer feldspar    18.5

Silica     11.5

Na2O  0.7%    Al2O3 24.5%      SiO2 69.5%

K2O  2.6%                               TiO2  1.5%

MgO  0.2%                              Fe2O3  0.9%

CaO  0.1%                              

Loss On Ignition:  6.7%

Shrinkage : 14%

Color : Medium brown

Water absorption : 0.1%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

-----------------------------

Stoneware Clay  #59

GoldArt    57

Bell Dark ball clay    27

Redart    14

Sand (60 mesh)      2

QIT Red Dust      1

Grog (48 mesh)      5

Na2O  0.2%    Al2O3 29.0%     SiO2 63.7%

K2O  1.3%                              P2O5  0.0%

MgO  0.4%                             TiO2  1.9%

CaO  0.2%                              Fe2O3  3.1%

  

Loss On Ignition:  8.3%

Shrinkage : 10.5%

Color : Dark brown

Water absorption : 0.6%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

--------------------------------

Stoneware Clay #60

Bell Dark ball clay    26

M&D Sledge ball clay    25

EPK    24

Custer feldspar    10

Silica    15

QIT Red Dust      2

Grog (48 mesh)    10

Na2O  0.4%    Al2O3 28.7%     SiO2 64.6%

K2O  1.4%                              P2O5  0.1%

MgO  0.2%                             TiO2  1.1%

CaO  0.4%                              Fe2O3  3.1%

Loss On Ignition:  7.8%

Shrinkage : 14%

Color : Buff

Water absorption : 4%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

----------------------------

Stoneware Clay #61

EPK    32
Custer feldspar    20
Bell Dark ball clay    30
Nepheline syenite    12
GoldArt      2
Silica      4

QIT Red Dust      2.4
Grog (30 mesh)      5
Grog (48 mesh)      5

Na2O  1.9%    Al2O3 30.7%     SiO2 60.1%

K2O  2.9%                              P2O5  0.1%

MgO  0.1%                             TiO2  0.9%

CaO  0.3%                              Fe2O3  3.0%

Loss On Ignition:  7.0%

Shrinkage : 14%

Color : Reddish medium brown

Water absorption : 0.1%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

--------------------------------

Stoneware Clay #62

GoldArt    50

Bell Dark ball clay    12

Redart    25

Custer feldspar      8

Silica      5

Grog (48 mesh)    10

Na2O  0.5%    Al2O3 27.1%     SiO2 64.7%

K2O  2.5%                              P2O5  0.1%

MgO  0.5%                             TiO2  1.6%

CaO  0.2%                              Fe2O3  2.9%

Loss On Ignition:  6.5%

Shrinkage : 14%

Color : Dark brown

Water absorption : 0.5%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

------------------------------

Stoneware Clay #63

GoldArt    60

Bell Dark ball clay    33

Redart      7

QIT Red Dust      1

Grog (48 mesh)      5

Na2O  0.2%    Al2O3 30.6%     SiO2 62.7%

K2O  1.1%                              P2O5  0.0%

MgO  0.3%                             TiO2  2.0%

CaO  0.2%                              Fe2O3  2.7%

Loss On Ignition:  8.8%

Shrinkage : 12%

Color : Medium brown

Water absorption : 0.8%

Plasticity : 10.0 (12)

Glaze behaviour : 11.0 (12)

-----------------------------

Stoneware Clay #64

GoldArt    67

Bell Dark ball clay    33

QIT Red Dust      1

Grog (48 mesh)      5

Na2O  0.2%    Al2O3 31.7%     SiO2 62.4%

K2O  0.9%                              TiO2  2.1%

MgO  0.2%                             Fe2O3  2.3%

CaO  0.2%                              

  

Loss On Ignition:  9.1%

Shrinkage : 12%

Color : Medeium brown

Water absorption : 0.25%

Plasticity : 10.0 (12)

Glaze behaviour : 11.0 (12)

-------------------------------

Stoneware Clay #65

GoldArt    67

Bell Dark ball clay    33

QIT Red Dust      1.5

Grog (48 mesh)      5

Na2O  0.2%    Al2O3 31.5%     SiO2 62.1%

K2O  0.9%                              TiO2  2.1%

MgO  0.3%                             Fe2O3  2.8%

CaO  0.2%                              

Loss On Ignition:  9.1%

Shrinkage : 12%

Color : Dark brown

Water absorption : 0.6%

Plasticity : 10.0 (12)

Glaze behaviour : 11.0 (12)

-----------------------------

Stoneware Clay #66

GoldArt    67
Bell Dark ball clay    33

QIT Red Dust      2
Grog (48 mesh)      5

Na2O  0.2%    Al2O3 31.4%      SiO2 61.8%
K2O  0.9%                               TiO2  2.1%
MgO  0.3%                              Fe2O3  3.2%
CaO  0.2%                            

Loss On Ignition:  9.1%

Shrinkage : 12%
Color : Black
Water absorption : 0.1%
Plasticity : 10.0 (12)
Glaze behaviour : 11.0 (12)

------------------------------

Stoneware Clay #67

GoldArt    36

Bell Dark ball clay    19

EPK    10

Custer feldspar    19.5

Silica    15.5

Atlas Brown Dust      2.6

Grog (48 mesh)    10

Na2O  0.7%    Al2O3 26.1%     SiO2 65.7%

K2O  2.4%                              P2O5  0.0%

MgO  0.3%                             TiO2  1.2%

CaO  0.3%                              Cr2O3  0.3%

MnO  0.2%                             Fe2O3  2.6%

NiO  0.1%                              

Loss On Ignition:  6.0%

Shrinkage : 10%

Color : Light brown

Water absorption : 0.1%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

-----------------------------

Stoneware Clay #68

GoldArt    54

Bell Dark ball clay    26

Redart    20

Grog (48 mesh)      5

Na2O  0.2%    Al2O3 29.1%     SiO2 63.7%

K2O  1.6%                              P2O5  0.0%

MgO  0.5%                             TiO2  1.9%

CaO  0.2%                              Fe2O3  2.7%

Loss On Ignition:  8.3%

Shrinkage : 12%

Color : Medium brown

Water absorption : 0.6%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

------------------------------

Stoneware Clay #69

GoldArt    70
Bell Dark ball clay    30

QIT Red Dust      2
Grog (48 mesh)      5

Na2O  0.2%    Al2O3 31.4%     SiO2 61.7%
K2O  0.9%                              TiO2  2.1%
MgO  0.3%                             Fe2O3  3.2%
CaO  0.2%                            


Loss On Ignition:  9.0%

Shrinkage : 12%
Color : Black
Water sabsorption : 0.1%
Plasticity : 10.5 (12)
Glaze behaviour : 10 (12)

----------------------------

Stoneware Clay #70

GoldArt    30

Bell Dark ball clay    20

Redart    25

Custer feldspar    10

Silica    15

Grog (48 mesh)      5

Na2O  0.5%    Al2O3 22.3%     SiO2 70.0%

K2O  2.5%                              P2O5  0.1%

MgO  0.5%                             TiO2  1.3%

CaO  0.2%                              Fe2O3  2.6%

Loss On Ignition:  5.8%

Shrinkage : 12%

Color : Medium brown

Water absorption : 0.5%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

-----------------------------

Stoneware Clay #71

GoldArt    50
Redart    30
Silica    20

Grog (48 mesh)    10

Na2O  0.3%    Al2O3 23.1%     SiO2 69.5%
K2O  1.8%                              P2O5  0.1%
MgO  0.6%                             TiO2  1.5%
CaO  0.1%                              Fe2O3  3.1%

Loss On Ignition:  5.5%

Shrinkage : 10%

Color : Dark brown

Water absorption : 0.3%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

-----------------------------

Stoneware Clay #72

EPK    28

Bell Dark ball clay    32

Redart    15

Silica    10

Custer feldspar    15

QIT Red Dust      1

Grog (48 mesh)    10

Na2O  0.6%    Al2O3 28.3%    SiO2 64.1%

K2O  2.4%                             P2O5  0.1%

MgO  0.4%                            TiO2  1.0%

CaO  0.3%                             Fe2O3  2.9%

  

Loss On Ignition:  7.2%

Shrinkage : 13%

Color : Medium brown

Water absorption : 0.1%

Plasticity : 10 (12)

Glaze behaviour : 12 (12)

------------------------------

Stoneware Clay #73

GoldArt    44
Bell Dark ball clay    23
Custer feldspar    14
Silica      9
Barnard slip    10

Na2O  0.6%    Al2O3 25.3%      SiO2 67.0%

K2O  2.3%                               TiO2  1.5%

MgO  0.2%                              Fe2O3  2.6%

CaO  0.2%                              

MnO  0.3%                              

Volatiles:

 Other  7.4%

Loss On Ignition:  6.9%

Shrinkage : 10%
Color : Dark brown
Water absorption : 0.1%
Plasticity : 10.5 (12)
Glaze behaviour : 12 (12)

-----------------------------

Stoneware Clay #74

GoldArt    45
Bell Dark ball clay    22
Custer feldspar      9
Silica      9
Redart    10
Barnard slip      5

Grog (48 mesh)    10

Na2O  0.5%    Al2O3 26.8%     SiO2 65.8%
K2O  2.0%                              P2O5  0.0%
MgO  0.4%                             TiO2  1.6%
CaO  0.2%                              Fe2O3  2.6%
MnO  0.2%                            

Loss On Ignition:  6.7%

Shrinkage : 12%

Color : Dark brown

Water absorption : 1.25%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

-----------------------------

Stoneware Clay #75

GoldArt    23
Bell Dark ball clay    23
Redart    10
Custer feldspar    23
Silica    14
Barnard slip      7

Grog (48 mesh)      5

Na2O  0.8%    Al2O3 21.7%     SiO2 69.8%
K2O  3.3%                              P2O5  0.0%
MgO  0.3%                             TiO2  1.1%
CaO  0.2%                              Fe2O3  2.5%
MnO  0.2%                            

Loss On Ignition:  5.3%

Shrinkage : 14%
Color : Dark brown
Water absorption : 1.5%
Plasticity : 10.5 (12)
Glaze behaviour : 12 (12)

-----------------------------

Stoneware Clay #76

GoldArt    53
Bell Dark ball clay    24
Custer feldspar      9
Silica      9
Barnard slip      5

Grog (48 mesh)      5

Na2O  0.4%    Al2O3 27.0%     SiO2 66.7%
K2O  1.7%                              TiO2  1.7%
MgO  0.2%                             Fe2O3  1.9%
CaO  0.1%                            
MnO  0.2%                            

Volatiles:
 Other  8.0%

Loss On Ignition:  7.4%

Shrinkage : 13%
Color : Dark brown
Water absorption : 0.5%
Plasticity : 10.5 (12)
Glaze behaviour : 12 (12)

------------------------------

Stoneware Clay #77

GoldArt    45
Bell Dark ball clay    18
Custer feldspar      9
Silica    18
Redart    10

QIT Red Dust      1
Grog (48 mesh)      5

Na2O  0.4%    Al2O3 23.5%     SiO2 69.6%
K2O  1.9%                              P2O5  0.0%
MgO  0.3%                             TiO2  1.4%
CaO  0.2%                              Fe2O3  2.6%

Loss On Ignition:  6.2%

Shrinkage : 14%
Color :Medium brown
Water absorption : 0.6%
Plasticity : 10.5 (12)
Glaze behaviour : 12 (12)

-------------------------------

Stonrware Clay #78

EPK    17
GoldArt    25
Bell Dark ball clay    17
Custer feldspar    16
Silica      8
Redart    10
Barnard slip      7

Grog (48 mesh)      5

Na2O  0.6%    Al2O3 26.4%      SiO2 65.6%

K2O  2.7%                               P2O5  0.1%

MgO  0.3%                              TiO2  1.2%

CaO  0.2%                               Fe2O3  2.7%

MnO  0.2%                              

Loss On Ignition:  7.1%

Shrinkage : 12%

Color :Dark brown

Water absorption : 0.5%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

------------------------------

Stoneware Clay #79

GoldArt    44

Bell Dark ball clay    19

Custer feldspar    18

Silica      9

Redart    10

QIT Red Dust      1

Grog (48 mesh)      5

Na2O  0.7%    Al2O3 25.0%     SiO2 66.9%

K2O  2.8%                              P2O5  0.0%

MgO  0.3%                             TiO2  1.4%

CaO  0.2%                              Fe2O3  2.6%

                              

Loss On Ignition:  6.2%

Shrinkage : 12%

Color :Medium brown

Water absorption : 0.3%

Plasticity : 10.5 (12)

Glaze behaviour : 11 (12)

-----------------------------

Stoneware Clay #80

GoldArt    45
Bell Dark ball clay    19
Custer feldspar    13
Silica    13
Redart    10

QIT Red Dust      1
Grog (48 mesh)      5

Na2O  0.6%    Al2O3 24.4%     SiO2 68.1%
K2O  2.3%                              P2O5  0.0%
MgO  0.3%                             TiO2  1.5%
CaO  0.2%                              Fe2O3  2.6%

Loss On Ignition:  6.3%

Shrinkage : 12%
Color :Medium brown
Water absorption : 1.5%
Plasticity : 10.5 (12)
Glaze behaviour : 11 (12)

----------------------------

Stoneware Clay #80

GoldArt    45
Bell Dark ball clay    19
Custer feldspar    13
Silica    13
Redart    10

QIT Red Dust      1

Grog (48 mesh)      5

Na2O  0.6%    Al2O3 24.4%     SiO2 68.1%

K2O  2.3%                              P2O5  0.0%

MgO  0.3%                             TiO2  1.5%

CaO  0.2%                              Fe2O3  2.6%

Loss On Ignition:  6.3%

Shrinkage : 12%

Color :Medium brown

Water absorption : 1.5%

Plasticity : 10.5 (12)

Glaze behaviour : 11 (12)

------------------------------

Stoneware Clay #81

M&D Sledge ball clay    27

EPK    36

Redart    10

Custer feldspar    13

Silica      9

Barnard slip      5

Grog (48 mesh)    10

Na2O  0.5%    Al2O3 30.0%     SiO2 62.7%

K2O  2.2%                              P2O5  0.1%

MgO  0.4%                             TiO2  0.8%

CaO  0.3%                              Fe2O3  2.8%

MnO  0.2%                              

Loss On Ignition:  7.9%

Shrinkage : 12%

Color :Dark brown

Water absorption : 0.6%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

------------------------------

Stoneware Clay #82

M&D Sledge ball clay    30

EPK    40

Alberta slip      5

Custer feldspar    15

Silica    10

QIT Red Dust      1.15

Grog (48 mesh)    10

Na2O  0.7%    Al2O3 30.9%     SiO2 61.8%

K2O  2.1%                              P2O5  0.1%

MgO  0.4%                             TiO2  0.7%

CaO  0.6%                              Fe2O3  2.7%

                              

  Loss On Ignition:  7.8%

Shrinkage : 11%
Color :Beige
Water absorption : 0.2%
Plasticity : 10.5 (12)
Glaze behaviour : 12 (12)

--------------------------------

Stoneware Clay #83

M&D Sledge ball clay    30
EPK    40
Alberta slip      5
Custer feldspar    15
Silica    10

QIT Red Dust      1.45

Grog (48 mesh)    10

Na2O  0.7%    Al2O3 30.9%     SiO2 61.6%

K2O  2.1%                              P2O5  0.1%

MgO  0.4%                             TiO2  0.7%

CaO  0.7%                              Fe2O3  2.9%

                              

 Loss On Ignition:  7.8%

Shrinkage : 11%

Color :Beige

Water absorption : 0.2%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

------------------------------

Stoneware Clay #84

M&D Sledge ball clay    30

EPK    40

Redart      5

Custer feldspar    15

Silica    10

QIT Red Dust      1.15

Grog (48 mesh)    10

Na2O  0.6%    Al2O3 31.1%     SiO2 61.9%

K2O  2.1%                              P2O5  0.1%

MgO  0.3%                             TiO2  0.8%

CaO  0.3%                              Fe2O3  2.8%

  

Loss On Ignition:  8.0%

Shrinkage : 11%

Color :Buff

Water absorption : 0.2%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

--------------------------------

Stoneware Clay #85

M&D Sledge ball clay    29

EPK    38

Redart    10

Custer feldspar    14

Silica      9

QIT Red Dust      1.15

Grog (48 mesh)    10

Na2O  0.6%    Al2O3 30.6%     SiO2 61.9%

K2O  2.2%                              P2O5  0.1%
MgO  0.4%                             TiO2  0.8%
CaO  0.3%                              Fe2O3  3.1%

Loss On Ignition:  7.9%

Shrinkage : 12%
Color :Brown
Water absorption : 0.9%
Plasticity : 10.5 (12)
Glaze behaviour : 12 (12)

------------------------------

Stoneware Clay #86

GoldArt    65
Bell Dark ball clay    22
Redart    10
Talc      2

QIT Red Dust      1.15

Grog (48 mesh)      5

Na2O  0.2%    Al2O3 29.7%     SiO2 62.4%
K2O  1.2%                              P2O5  0.0%
MgO  1.0%                             TiO2  2.0%
CaO  0.4%                              Fe2O3  3.1%
                       
Loss On Ignition:  8.5%

Shrinkage : 12%
Color :Medium brown
Water absorption : 1.4%
Plasticity : 10.5 (12)
Glaze behaviour : 12 (12)

-------------------------------

Stoneware Clay #87

M&D Sledge ball clay    30

EPK    40

Redart      5

Custer feldspar    15

Silica    10

QIT Red Dust      1.4

Grog (48 mesh)    10

Na2O  0.6%    Al2O3 31.0%     SiO2 61.8%

K2O  2.1%                              P2O5  0.1%

MgO  0.3%                             TiO2  0.8%

CaO  0.4%                              Fe2O3  3.0%

Loss On Ignition:  8.0%

Shrinkage : 12%

Color :Medium brown

Water absorption : 0.2%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

------------------------------

Stoneware Clay #88

GoldArt    57

Bell Dark ball clay    27

Redart    14

Sand (60 mesh)      2

Na2O  0.2%    Al2O3 28.1%     SiO2 65.6%

K2O  1.4%                              P2O5  0.0%

MgO  0.4%                             TiO2  1.9%

CaO  0.2%                              Fe2O3  2.2%

Loss On Ignition:  8.8%

Shrinkage : 10.5%

Color :Medium brown

Water absorption : 0.6%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

---------------------------------

Stoneware Clay #89

GoldArt    60

Bell Dark ball clay    33

Redart      7

QIT Red Dust      1.15

Grog (48 mesh)      5

Na2O  0.2%    Al2O3 30.6%     SiO2 62.6%

K2O  1.1%                              P2O5  0.0%

MgO  0.3%                             TiO2  2.0%

CaO  0.2%                              Fe2O3  2.9%

Loss On Ignition:  8.8%

Shrinkage : 12%

Color :Light orange

Water absorption : 0.8%

Plasticity : 10.0 (12)

Glaze behaviour : 12 (12)

-----------------------------

Stoneware Clay #90

GoldArt    67

Bell Dark ball clay    33

QIT Red Dust      1.15

Grog (48 mesh)      5

Na2O  0.2%    Al2O3 31.6%     SiO2 62.3%

K2O  0.9%                              TiO2  2.1%

MgO  0.2%                             Fe2O3  2.5%

CaO  0.2%                              

Loss On Ignition:  9.1%

Shrinkage : 12%

Color :Medium buff

Water absorption : 0.2%

Plasticity : 10.0 (12)

Glaze behaviour : 12 (12)

------------------------------

Stoneware Clay #91

GoldArt    67
Bell Dark ball clay    33

QIT  Red Dust      1.7
Grog (48 mesh)      5

Na2O  0.2%    Al2O3 31.4%     SiO2 62.0%
K2O  0.9%                              TiO2  2.1%
MgO  0.3%                             Fe2O3  2.9%
CaO  0.2%                            

Loss On Ignition:  9.1%

Shrinkage : 12%
Color :Medium buff
Water absorption : 0.6%
Plasticity : 10.0 (12)
Glaze behaviour : 12 (12)

-----------------------------

Stoneware Clay #92

GoldArt    67
Bell Dark ball clay    33

QIT Red Dust      2.3
Grog (48 mesh)      5

Na2O  0.2%    Al2O3 31.3%     SiO2 61.6%
K2O  0.9%                              TiO2  2.1%
MgO  0.3%                             Fe2O3  3.4%
CaO  0.3%                            

Loss On Ignition:  9.1%

Shrinkage : 12%
Color :Orange
Water absorption : 0%
Plasticity : 10.0 (12)
Glaze behaviour : 12 (12)

-------------------------------

Stoneware Clay #93

GoldArt    70
Bell Dark ball clay    30

QIT Red Dust      2.3
Grog (48 mesh)      5

Na2O  0.2%    Al2O3 31.3%     SiO2 61.5%
K2O  0.9%                              TiO2  2.1%
MgO  0.3%                             Fe2O3  3.4%
CaO  0.2%                            

Loss On Ignition:  9.0%

Shrinkage : 12%
Color :Orange brown
Water absorption : 0%
Plasticity : 10.0 (12)
Glaze behaviour : 12 (12)

-----------------------------

Stoneware Clay #94

EPK    28
Bell Dark ball clay    32
Redart    15
Silica    10
Custer feldspar    15

QIT Red Dust      1.15
Grogf (48 mesh)    10

Na2O  0.6%    Al2O3 28.3%     SiO2 64.0%
K2O  2.4%                              P2O5  0.1%
MgO  0.4%                             TiO2  1.0%
CaO  0.3%                              Fe2O3  3.0%

Loss On Ignition:  7.2%

Shrinkage : 13%

Color :Medium brown

Water absorption : 0%

Plasticity : 10.0 (12)

Glaze behaviour : 12 (12)

------------------------------

Stoneware Clay #95

GoldArt    45

Bell Dark ball clay    18

Custer feldspar      9

Silica    18

Redart    10

QIT Red Dust      1.15

Grog (48 mesh)      5

Na2O  0.4%    Al2O3 23.4%     SiO2 69.6%

K2O  1.9%                              P2O5  0.0%

MgO  0.3%                             TiO2  1.4%

CaO  0.2%                               Fe2O3  2.7%

  

Loss On Ignition:  6.2%

Shrinkage : 14%

Color :Medium brown

Water absorption : 0.6%

Plasticity : 10.0 (12)

Glaze behaviour : 12 (12)

-----------------------------

Stoneware Clay #96

GoldArt    44

Bell Dark ball clay    19

Custer feldspar    18

Silica      9

Redart    10

QIT Red Dust      1.15

Grog (48 mesh)      5

Na2O  0.7%    Al2O3 25.0%     SiO2 66.8%

K2O  2.8%                              P2O5  0.0%

MgO  0.3%                             TiO2  1.4%

CaO  0.2%                              Fe2O3  2.7%

  

Loss On Ignition:  6.2%

Shrinkage : 12%

Color :Medium brown

Water absorption : 0.3%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

------------------------------

Stoneware Clay #97

GoldArt    45

bell daek ball clay    19

Custer feldspar    13

Silica    13

Redart    10

QIT Red Dust      1.15

Grog (48 mesh)      5

Na2O  0.6%    Al2O3 24.4%     SiO2 68.0%

K2O  2.3%                              P2O5  0.0%

MgO  0.3%                             TiO2  1.5%

CaO  0.2%                             Fe2O3  2.7%

Loss On Ignition:  6.3%

Shrinkage : 12%

Color :Medium brown

Water absorption : 1.5%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

-------------------------------

Stoneware Clay #98

GoldArt    36

Bell Dark ball clay    19

EPK    10

Custer feldspar    19.5

Silica    15.5

Atlas Brown Dust      3.6

Grog (48 mesh)    10

Na2O  0.7%    Al2O3 25.8%     SiO2 65.1%

K2O  2.4%                              P2O5  0.0%

MgO  0.3%                             TiO2  1.2%

CaO  0.4%                              Cr2O3  0.5%

MnO  0.2%                             Fe2O3  3.1%

NiO  0.2%                              

Loss On Ignition:  5.9%

Shrinkage : 10%

Color :Dark brown

Water absorption : 0%

Plasticity : 10.5 (12)

Glaze behaviour : 12 (12)

--------------------------------

Stoneware Clay #99

GoldArt    55

Redart    30

Silica    15

Grog (48 mesh)    10

Na2O  0.3%    Al2O3 24.6%     SiO2 67.7%

K2O  1.9%                              P2O5  0.1%

MgO  0.6%                             TiO2  1.6%

CaO  0.1%                             Fe2O3  3.2%

Loss On Ignition:  5.9%

Shrinkage : 10%

Color :Dark brown

Water absorption : 2.5%

Plasticity : 10.0 (12)

Glaze Behaviour : 12 (12)

-----------------------